通过制备不同晶相结构〔单斜相(m-ZrO_2)、四方相(t-ZrO_2)和无定型(a-ZrO_2)〕ZrO_2载体,再通过沉积沉淀法制得Cu/m-ZrO_2、Cu/t-ZrO_2和Cu/a-ZrO_2催化剂,分别用于催化二乙醇胺脱氢合成亚氨基二乙酸反应。采用XRD、氮气物理吸附脱附、XPS、H_2-TPR、CO_2-TPD对催化剂的结构进行了表征。结果表明,Cu/m-ZrO_2催化剂界面更加有利于Cu~+/Cu~0稳定存在,具有更多的碱性位点,且抗氧化性较好。在二乙醇胺脱氢反应中,Cu/m-ZrO_2催化剂性能最好,反应时间为2.5 h,亚氨基二乙酸收率为97.64%。     

高伸长率冷轧双相钢DP980显微组织及性能

摘要：为了进一步提高冷轧双相钢DP980的强塑性，采用低C-Si-Mn-Nb-Cr成分，通过调整连续退火工艺参数，系统研究了工艺组织性能的关系，利用OM、SEM、EBSD分析了不同退火温度条件下各相的比例、尺寸、形貌、分布，同时利用力学拉伸试验手段研究了连退两相区退火温度对强塑性的影响。结果表明，通过优化调整连续退火工艺，不仅可以在冷轧铁素体和马氏体双相钢的组织上获得少量的残余奥氏体，也能细化再结晶晶粒，最终获得ReL/Rm≤0.5、高伸长率A50≥15%的冷轧DP980，提高强塑性的同时改善了成型性能。     

Poly(L-lysine)-poly(ethylene glycol) layers with different structure and their influence on silica suspension stability

The effects of the structure of di- and triblock copolymers of poly(L-lysine) – LYS with poly(ethylene glycol) – PEG as well as the length of nonionic fragment in the LYS-PEG macromolecule on the copolymer chains conformation in the adsorption layer formed on the colloidal silica (SiO2) surface were examined. Spectrophotometry and turbidimetry were applied for the determination of copolymer adsorbed amounts and stability coefficients of silica aqueous suspensions. The electrokinetic parameters such as solid surface charge density and zeta potential were also estimated. The adsorption of LYS-PEG was proved to be the highest at pH 10 whereas the lowest adsorption on the solid surface was found for the triblock copolymer with long fragments of LYS at the same pH value.     

Investigations of geometrical structure and morphology of samples made of hard machinable materials after wire electrical discharge machining and vibro‐abrasive finishing

In this article the results concerned influence of processing conditions of the wire electrical discharge machining and vibro‐abrasive machining on the surface layer and morphology of samples made of hard machinable materials used in aircraft industry like: Titanium 5553 β, Inconel 617, Hastelloy X and Magnesium AZ31 have been presented. For this purpose the cubic and cylindrical samples made of hard machinable alloys have been prepared using optimal electric parameters of wire‐cut electrical discharge machining and finally they have been polished using circular vibratory finishing technology and different ceramic shaped stones.     

Unique crystal structures and their applications as materials for Li1+x-yM1-x-3yTix+4yO3 (M = Nb or Ta, 0.07 ≤ x ≤ 0.33, 0 ≤ y ≤ 0.175)

In the Li₂O–M₂O₅–TiO₂ (M = Nb or Ta) system, Li_1+x-yM_1-x-3yTi_x+4yO₃ (LMT) forms with a superstructure known as the M-phase, in which the periodical intergrowth layers are inserted in a matrix having a trigonal structure of LiMO₃. We have been investigating this unique material focusing on its crystal structure, photoluminescence, and electrical properties.First, the formation area of the superstructure was compared between Nb- and Ta- systems and the difference was accurately analyzed.Second, to apply this unique material as a host material of phosphor, we synthesized new phosphors with various emission colors. Red phosphor, having a high PL intensity with an internal quantum efficiency of 98%, was successfully synthesized and used as a host material of the solid solution for the Ta system. Its high value was the result of the large centroid-to-cation distance of the Eu³⁺ position in the [(Li, Eu)O₁₂] polyhedral.Further still, toward application of the unique qualities of an electro-ceramic, we successfully fabricated oriented balk ceramics for the Nb system by slip casting in a strong magnetic field of 12 T. As a result, anisotropic electric properties were found along the c-axis, which were caused by the superstructure. We first clarified the mechanism showing that the anisotropic Qf value was due to anisotropic electron conductivity and anisotropic bonding strength within the superstructure.     

耐蚀合金中TiN析出机制

摘要：TiN颗粒尺寸及其分布对耐蚀合金性能有明显的影响，因此有必要对TiN在铸坯中的分布及其析出行为进行研究。采用扫描电镜(SEM)、金相显微镜（OM）观察了TiN夹杂物在铸坯中的分布、尺寸及其形貌；基于热力学和动力学理论分析了耐蚀合金铸坯中TiN夹杂物的析出时机及其尺寸，结合试验结果和理论计算明确了TiN夹杂物在凝固后铸坯中的位置和尺寸与析出时机的关系，为控制TiN夹杂物提供理论指导。结果表明，冶炼过程中析出的TiN夹杂物尺寸较大，在凝固过程中被枝晶吞没，位于铸坯枝晶内和等轴晶内；微观偏析计算结果表明，在凝固分数为0.55时，TiN开始析出，最开始析出TiN夹杂物的逐渐长大，长大后的TiN易于被二次枝晶吞没，最终位于铸坯中的枝晶间和等轴晶内，后期析出的TiN则在枝晶间和等轴晶间。固相中析出的TiN夹杂物长大较慢，尺寸细小，最终位于奥氏体晶界。     

Study on the long-term behaviour of glass fibre in the tensile stress field

Glass fibre is a random network structure composed of [SiO₄] tetrahedra. The structure contains a large number of defects, which act as crack initiation points. Under tensile stress, cracks undergo crack initiation, stable propagation, failure propagation, and fracture, and the stress that begins after unstable propagation is called the critical fracture stress. When the stress is less than the critical value, the crack is subject to the force of chemical bonds during the crack propagation process, and crack arrest occurs. When the stress is greater than the critical value, the glass fibre will undergo destructive fracture. In this paper, long-term tensile tests were carried out on glass fibre and a glass fibre composite under different constant tensile stress conditions. The fracture times of the glass fibre and glass fibre composite under different tensile stresses were obtained, the critical fracture stress of glass fibre was inferred, and the fracture mechanism was explained.     

Hydrolysis-resistant polyurethane elastomers synthesized from hydrophobic bio-based polyfarnesene diol

Hydrolytic stability is an essential requirement for polyurethanes (PUs) that are used in highly humid and aqueous environments. In this study, hydrolysis-resistant PU elastomers (PUEs) are synthesized based on hydrophobic bio-based polyfarnesene diol (PFD), which contains unique “bottle brushes” structure (with long branched hydrocarbon side chains). The effect of hard segment (HS) content, ranging from 30 to 50%, on the morphology and properties of PUEs is investigated by Fourier transform infrared spectroscopy, thermogravimetric analysis, differential scanning calorimetry, X-ray diffraction, scanning electron microscopy, tensile, water absorption, and contact angle measurements. The results show that there are prominent phase separations in the synthesized PUEs. The PUEs show a three-stage degradation process and two T_g, one is at about −66 °C and the other 61 °C, which are related to the soft segment and HS, respectively. Water contact angles of PUEs increase from 98.6 to 105.2° with the increasing of PFD structural unit fraction. After being immersed in deionized water for 30 days, PUEs show no significant degradation of both tensile strength and elongation at break, and mass changes of all samples are less than 0.5%. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47673.     

Remediation of oil spill polluted water from Niger Delta Nigeria by sorption onto ammonium sulfate modified Dialium guineense seed husk

The abstraction of crude oil molecules from aqueous solution (produced water) and from real petroleum polluted water (collected from River State, Nigeria) by Dialium guineense Seed Husk (DGSH) and its ammonium sulfate functionalized form (AS-DGSH) was studied using a batch technique. The sorbents were characterized using Fourier transform infrared (FTIR), BET surface area analysis and the Scanning electron microscopy (SEM). Crude oil characterization revealed a light crude oil based on the API gravity of 35.6⁰. The Langmuir and Freundlich models gave good fits for crude oil sorption on DGSH and AS-DGSH respectively. The sorbents were found to remove over 50% of crude oil from the real polluted water at the natural pH of 6.1 and showed increase in removal with increase in sorbent dose. The potential of DGSH and its ammonium sulfate modified derivative as effective low cost sorbents for oil spill treatment was established.     

Improving room-temperature electrochemical performance of solid-state lithium battery by using electrospun La2Zr2O7 fibers-filled composite solid electrolyte

Low ionic conductivity at room temperature and poor interfacial compatibility are the main obstacles to restrain the practical application of polymer solid electrolytes. In this work, lanthanum zirconate (LZO) fibers were prepared by electrospinning method and used for the first time as fillers in sandwich polypropylene carbonate (PPC)-based solid electrolyte. Meanwhile, a graphite coating was applied on one surface of the composite solid electrolyte (CSE) membrane. The results show that the LZO fibers significantly increases the room-temperature electrochemical performance of the CSE, and the graphite coating enhances the interfacial compatibility between electrolyte and lithium anode. Furthermore, an ultra-thin PPC-LZO CSE with a total thickness of 22 μm was prepared and used in NCM622/CSE/Li solid-state cell, which shows an initial discharge capacity of 165.6 mAh/g at the current density of 0.5C and a remaining capacity of 113.0 mAh/g after 250 cycles at room temperature. Rise to 1C, the cell shows an initial discharge capacity of 154.2 mAh/g with a remaining capacity of 95.6 mAh/g after 250 cycles. This ultra-thin CSE is expected to be widely applied in high energy-density solid-state battery with excellent room-temperature electrochemical performances.